Luting II is a universal restorative material with proven GIC properties functioning as both filling and luting. Different functions are achieved according to the adjustment of the powder-to-liquid ratio.
Indications
• Cementation of metal-based inlays, onlays, crowns and bridges.
• Cementation of high strength (zirconia based), all ceramic crowns and bridges.
• Cementation of posts and screws made of metal or high-strength ceramic.
• Cementation of orthodontic bands.
• Restoration of caries in unstressed area.
Advantages
• Good Durability
The higher compression capacity (> 180Mpa) ensures good durability.
• When used for luting: Ideal film thickness
• When used for filling:
• Good durability
• Low stickiness
• Time saving
Technical Parameters
| Items | For luting | For filling |
| Powder/liquid ratio (g/g) | 1.6 ~ 1.8/1.0 | 2.3~ 2.5/1.0 |
| Mixing time (min., sec.) | 45" | 45" |
| Working time (min., sec.) | 2'10" | 3'00" |
| (at 23℃)(from start of mixing) | ||
| Net setting time | 3'15" | 2'45" |
| Compressive capability | ＞140MPa (ISO ≥ 50 MPa) | ＞180MPa (ISO ≥ 100 MPa) |
| Film Thickness | 13μm | / |
Standard Package
| 30g*1 | Powder |
| 25g*1 | Liquid |
| 1 | Measuring scoop |
| 1 | Mixing pad(50 sheets) |