Indication
Cementation of all sorts of dental restorations including crowns, bridges, inlays/onlays, veneers, dental posts and other restorations made from materials of metals/alloys, mental-ceramic, all-ceramic and/or porcelain, composites, and their combinations.
Advantages
• Dual cure offers flexible options:
Suitable for both dual cure and light cure.
• Sufficient working time and fast setting time:
Sufficient work time: leave enough time for doctors to prepare before they put everything into the patient's mouth.
Short curing time: avoid any unexpected movement or shift of the restoration after doctors have placed it into the patient's mouth.
• High flexural strength:
After curing it shows excellent physical and mechanical properties. Indicators such as flexural strength, film thickness, solubility and water absorption are better than most mainstream products in the market.
• Low film thickness, solubility and water absorption
• 3 opacity and 7 shades available:
With 3 opacity and 7 shades, satisfies the needs of both high translucency and shades covering, suitable for cementation of restorations with different color requirements.
• Impressive radiopacity, X-ray radiation resistance could be over 400%.
Technical Parameter
| ISO1042:2009 | TopCEM | |
| Flexural strength/MPa (Dual cure) | ＞50 | 112.7 |
| Flexural strength/MPa (Self cure) | ＞50 | 107.5 |
| Solubility/ug/mm3 (Dual cure) | ＜7.5 | 1.8 |
| Water absorption/ug/mm3 (Dual cure) | ＜40 | 19.8 |
| Film thickness/μm | ＜50 | 20 |
| Work time(23±1)℃ | ＞60s | Qualified |
| Setting time(37±1)℃ | ＜10min | 2′38″ |
| Radioactive resistance(%) | ＞100 | 400 |
Technical Parameter
| TopCEM | |
| Bonding strength to enamel/MPa | 19.5 |
| Bonding strength to dentin/MPa | 22.4 |
| Bonding strength to zirconia/MPa | 27.7 |
| Bonding strength to cobalt chromium metal/MPa | 20.7 |
| Bonding strength to glass ceramics/MPa | 21.8 |
Packaging
| 8g*1/8g*1+mixing tips | Syringe |